谭海燕,孟泽,冯翰林,胡卫兵,吴得勇,谭学才.TiO2/MIL-53(Al)和TiO2/Al2O3催化剂的制备及其光催化性能研究[J].华中农业大学学报,2020,39(3):68-74
TiO2/MIL-53(Al)和TiO2/Al2O3催化剂的制备及其光催化性能研究
Preparation of TiO2/MIL-53(Al) and TiO2/Al2O3 catalysts and their photocatalytic performance
投稿时间:2019-07-22  
DOI:
中文关键词:  金属有机骨架材料  次甲基蓝  污水处理  光催化降解  去除率
英文关键词:metal-organic framework  submethyl blue  sewage treatment  photocatalytic degradation  removal rate
基金项目:国家自然科学基金项目(21769009);湖北省恩施州科技局指导性项目(恩州科业\[2018\]19号);生物资源保护与利用湖北省重点实验室(PKLHB1706);广西林产化学与工程重点实验室开放项目(GXFK1904);广西科技基地和人才专项(桂科AD 18126005);湖北省“双一流”建设专项
作者单位E-mail
谭海燕 生物资源保护与利用湖北省重点实验室/湖北民族大学化学与环境工程学院恩施 445000
广西民族大学广西林产化学与工程重点实验室南宁 530006 
Jftanhaiyan@sina.com 
孟泽 生物资源保护与利用湖北省重点实验室/湖北民族大学化学与环境工程学院恩施 445000  
冯翰林 生物资源保护与利用湖北省重点实验室/湖北民族大学化学与环境工程学院恩施 445000  
胡卫兵 生物资源保护与利用湖北省重点实验室/湖北民族大学化学与环境工程学院恩施 445000  
吴得勇 生物资源保护与利用湖北省重点实验室/湖北民族大学化学与环境工程学院恩施 445000  
谭学才 广西民族大学广西林产化学与工程重点实验室南宁 530006 gxunxctan@126.com 
摘要点击次数: 45
全文下载次数: 36
中文摘要:
      采用溶剂热法合成了MIL-53(Al),以此为载体负载TiO2制备得到TiO2/MIL-53(Al)光催化剂用于污水中次甲基蓝的催化降解研究,并与传统载体材料Al2O3负载的TiO2催化剂的光催化效果进行比较。样品通过热重-差热扫描量热(TG-DSC)、红外光谱(FTIR)、扫描电镜(SEM)、X 射线衍射(XRD)、N2物理吸附-脱附等方法进行表征。采用光度吸收法分析污水中次甲基蓝的降解率,结果显示,TiO2/MIL-53(Al)光催化剂对次甲基蓝的光催化降解率达到98.6%,而TiO2/Al2O3光催化剂对次甲基蓝的降解率只有70.3%,TiO2/MIL-53(Al)光催化剂对污水中次甲基蓝的降解去除能力明显优于TiO2/Al2O3光催化剂对次甲基蓝的降解去除能力。
英文摘要:
      MIL-53 (Al) was synthesized by solvothermal method, and TiO2/MIL-53 (Al) photocatalyst was prepared by using TiO2 as the carrier for the catalytic degradation of methine blue in sewage. The photocatalytic performance of the TiO2/MIL-53(Al) and the TiO2/Al2O3 was compared. The catalysts were characterized by thermogravimetric-differential scanning calorimeter (TG-DSC), Fourier transform infrared(FTIR) spectroscopy, scanning electron microscopy (SEM), X-ray diffraction (XRD) and N2 adsorption-desorption. The photodegradation efficiency of submethyl blue was analyzed by photometric absorption method. The results showed that the degradation rate of methylene was more than 98.6% on TiO2/MIL-53(Al) photocatalyst, but that of methylene was only 70.3% on TiO2/Al2O3 photocatalyst. Therefore, the photocatalytic activity of TiO2/MIL-53(Al) photocatalyst exhibited much higher than that of the TiO2/Al2O3 photocatalyst in degradating methyl blue.